Characterization of the substitution pattern of cellulose derivatives using carbohydrate-binding modules

Abstract

Background

Derivatized celluloses, such as methylcellulose (MC) and hydroxypropyl methylcellulose (HPMC), are of pharmaceutical importance and extensively employed in tablet matrices. Each batch of derivatized cellulose is thoroughly characterized before utilized in tablet formulations as batch-to-batch differences can affect drug release. The substitution pattern of the derivatized cellulose polymers, i.e. the mode on which the substituent groups are dispersed along the cellulose backbone, can vary from batch-to-batch and is a factor that can influence drug release.

Results

In the present study an analytical approach for the characterization of the substitution pattern of derivatized celluloses is presented, which is based on the use of carbohydrate-binding modules (CBMs) and affinity electrophoresis. CBM4-2 from Rhodothermus marinus xylanase 10A is capable of distinguishing between batches of derivatized cellulose with different substitution patterns. This is demonstrated by a higher migration retardation of the CBM in acrylamide gels containing batches of MC and HPMC with a more heterogeneous distribution pattern.

Conclusions

We conclude that CBMs have the potential to characterize the substitution pattern of cellulose derivatives and anticipate that with use of CBMs with a very selective recognition capacity it will be possible to more extensively characterize and standardize important carbohydrates used for instance in tablet formulation.

Background

Cellulose is the most abundant natural biopolymer on earth [1]. It is primarily used to produce paper but as it is renewable and abundant, cellulose is also an attractive raw material for various industrial uses. However, native cellulose from plants and wood has a crystalline structure that complicates its use in bioprocesses. It consists of glucose saccharides bonded through glycosidic 1–4 β-bonds (Figure 1) to form linear polymer chains that have very strong inter-chain attractions making the complex insoluble [2]. Chemical modification of cellulose resulting in the incorporation of functional groups at the free hydroxyl groups along the cellulose chains improves the solubility of the carbohydrate [3].

Figure 1
figure 1

Chemical structure of different celluloses derivatives. A. Cellulose consists of glucose saccharides connected through glycosidic 1–4 bonds. In the generation of cellulose derivatives hydrogen atoms (annotated as R) on three hydroxyl groups on each glucose unit are susceptible to chemical derivatization. The possible substitutions for hydroxypropyl methylcellulose (HPMC), methylcellulose (MC), hydroxypropyl cellulose (HPC), hydroxyethyl cellulose (HEC) and carboxymethyl cellulose (CMC) are shown. B. Schematic illustration of substitution patterns in homogenously and heterogeneously substituted cellulose.

Derivatized cellulose is used in a wide range of industries and included in food, textile, healthcare and personal care products. In the pharmaceutical industry derivatized celluloses are often used as excipients [1]-[3]. A common formulation is mixing of the active substance with a polymer in a compressed tablet that upon hydration swells into a gel from which a controlled, prolonged delivery of the drug occurs [4],[5]. Hydroxypropyl methylcellulose (HPMC) is the most frequently used polymer in such tablets [6], but other cellulose ethers with different patterns of substitutions are also commonly used (Figure 1), such as methylcellulose (MC), hydroxypropyl cellulose (HPC), hydroxyethyl cellulose (HEC) and carboxymethyl cellulose (CMC) [1],[5],[6].

The physicochemical properties of the derivatized polymer chains have been shown to affect their behavior and applicability as excipients in tablets [4]. An important factor affecting polymer behavior and drug release has been shown to be the average molecular weight that e.g. influences the viscosity of the dissolving tablets [7]-[10]. Other critical factors observed are the type and degree of substitution as well as the average number and position of the substituents in a single glucose unit [11]-[14]. In studies by Viridén et al. [15],[16], tablets produced from seven different commercial HPMC batches were investigated. The batches had the same substitution grade and viscosity but behaved differently with respect to their capacity for gelation and polymer release and it was concluded that these differences were correlated to the substitution pattern of the HPMC batches. In a later study, Viridén et al. also showed that the drug release mechanism in HPMC tablets is controlled to a greater extent by erosion if the HPMC has a substitution pattern that is homogeneous, while it is largely controlled by diffusion if the HPMC has a more heterogeneous substitution pattern [17]. Thus it is important to be able to characterize the raw material used as excipient in tablets in order to minimize batch-to-batch variation in the tablet production process.

Though methods for determining the localization of substitutions within a glucose unit are well established [18]-[20], the characterization of the substitution pattern along the glucose backbone is more challenging and often involves a combination of several techniques. Many of the approaches require partial hydrolysis of the derivatized cellulose chains, which can be performed either randomly, by chemical strategies [21], or by using hydrolyzing enzymes that cleave the chains at specific regions [22]. After partial hydrolysis, the chemical structures of the resulting oligomers are often analyzed using methods such as mass spectrometry (MS) or nuclear magnetic resonance NMR [23]. MS analyses have been performed both with matrix-assisted laser desorption/ionization time of flight (MALDI-TOF) mass spectrometry [13] as well as with electrospray ionization (ESI), with or without separation with liquid chromatography [12],[24],[25]. Such analyses have in turn been performed either with or without prior isotopic labeling [26],[27]. Other strategies differentiate the modified cellulose polymers by use of their cloud point, i.e. the gelation temperature, which partly depends on the substitution pattern [28],[29].

Enzyme-aided characterization of cellulose derivatives is an attractive approach as it is based on specific protein-carbohydrate interactions [30]. Other proteins that can specifically recognize natural cellulose are carbohydrate-binding modules (CBMs). CBMs are defined as non-catalytic modules of carbohydrate active enzymes that have a continuous polypeptide chain and a separate fold and display carbohydrate-binding activity [31]. In the present study it was investigated if the specificity in natural and engineered CBMs can be used for characterization of the substitution pattern of cellulose derivatives by affinity electrophoresis (AE). Two natural CBMs with reported ability to bind to cellulose oligomers and regenerated cellulose were used, CBM4-2 [32] and CBM28 [33]. In addition, three mutants derived from CBM4-2 were used, of which A-6 was selected for its binding to Avicel [34], X-2 L110F for its binding to several polysaccharides including β-glucan and cellulose oligomers [35], and G-4 for its lack of binding to carbohydrates (i.e. it serves as a negative control) [34],[36]. The mutants had been engineered for other studies and differ from CBM4-2 by a set of 7 to 9 mutations (Table 1) mostly found in the binding cleft. Also, because it is known that CBMs arranged in tandem often display a higher apparent affinity (avidity) for their target [37], a construct consisting of two connected CBM4-2 modules was included in the study. Altogether, these CBMs represent a collection of modules with different properties likely to represent different patterns of derivatized cellulose recognition.

Table 1 Amino acid differences existing between CBM4-2 and mutants thereof

Through these studies we are able to conclude that CBMs have the potential to discriminate between heterogeneously and homogeneously derivatized celluloses and envisage that such modules can be employed in the characterization of the substitution pattern of cellulose derivatives to be utilized for example in tablet formulations.

Results

Migration retardation of a set of CBMs was investigated by AE to evaluate if CBMs can distinguish between derivatized celluloses with a homogenous substitution pattern, i.e. randomly dispersed, from those with a heterogeneous substitution pattern, i.e. more clustered substitutions.

CBM4-2 and X-2 L110F distinguish between batches of MC with different substitution patterns

Non-denaturing electrophoresis demonstrated that CBM4-2 was retained more in the gels containing the heterogeneously substituted MC 1.78 or MC 1.80 than in the gel with homogeneously substituted MC 1.76 (Figure 2). CBM G-4, a carbohydrate non-binding negative control variant of CBM4-2, was as expected not retained in any of the gels. Of the other CBMs tested, A-6 and X-2 L110F were retained in all of the gels containing MC. X-2 L110F is retained more in the gels containing MC 1.80 and MC 1.78 than MC 1.76 although the difference in mobility is not as apparent as for CBM4-2. In contrast, A-6 is not able to make a distinction between the different MCs illustrating that by using different CBMs it is possible to get different views of the MCs.

Figure 2
figure 2

Affinity electrophoresis with three methylcellulose batches. The three batches have similar degree of substitution (1.76, 1.78 and 1.80 and denoted accordingly) however their substitution pattern differs. MC 1.76 is more homogeneously substituted while MC 1.78 and MC 1.80 have substitution patterns that are more heterogeneous. Three CBMs and a negative control (G-4) were run on native acrylamide gels containing one of each methylcellulose batch. CBM4-2 is more retained in the gels containing MC 1.78 or MC 1.80 compared to MC 1.76. A-6 and X-2 L110F are less discriminating and are retained in all gels containing methylcellulose. None of the CBMs were retained in the control gel containing no methylcellulose.

CBM4-2 distinguishes between HPMC batches with different substitution pattern

Gels containing four types of HPMCs were also analyzed for their ability to interact with the CBMs. Of the four different batches included, two of the HPMCs are classified as homogeneously substituted and the other as heterogeneously substituted. In this experiment the CBMs investigated were a negative control (G-4), CBM4-2, X-2 L110F and CBM28 from B. akibai Cel5A. The retardations were modest yet a distinction was observed for batches with a heterogeneous versus a homogeneous substitution pattern (Figure 3). In gels containing heterogeneously substituted HPMC, CBM4-2 was retained and the protein band had a trailing shape. In contrast, in gels containing HPMC with a homogeneous substitution pattern, CBM4-2 was hardly retained at all.

Figure 3
figure 3

Affinity electrophoresis with four hydroxypropyl methylcellulose batches. Two of the batches (20 and 22) are known to have a heterogeneous substitution pattern and the other two (21 and 23) a homogeneous substitution pattern. Three CBMs (CBM28, X-2 L110F and CBM4-2) and a negative control (G-4) were run in 17% acrylamide gels containing no or 1 mg/ml HPMC. Also a tandem CBM construct of CBM4-2:CBM4-2 together with a tandem negative control (G-4:G-4) were included in the assay. The retardation of the CBMs is modest but differences in mobility can be seen for CBM4-2 and CBM28 in gels containing HPMC of heterogeneous substitution pattern as compared to in gels with HPMC of homogeneous substitution pattern. The difference in retardation is more distinct for the tandem CBM4-2 construct.

Tandem CBM4-2 construct showed improved interaction with derivatized celluloses

In an effort to achieve better retardation a tandem CBM construct with possible higher apparent affinity to the cellulose derivatives due to avidity effects was generated. CBM4-2 was selected for this experiment as it appeared to be the CBM that is best capable of making a distinction between homogeneously and heterogeneously derivatized cellulose. The tandem construct consisted therefore of two CBM4-2 molecules linked together through a polypeptide linker. Indeed the difference in mobility for the tandem CBM in gels containing homogenously versus heterogeneously derivatized HPMC was more apparent than for the single CBM (Figure 3). It is thus possible to through engineering devise CBM constructs with enhanced ability to distinguish between batches of derivatized cellulose that carry either evenly or clustered distribution of substituents along the glucosyl backbone.

Discussion

Proof-of-concept - CBM have the potential to characterize cellulose derivatives

Cellulases are commonly employed for the characterization of derivatized celluloses with respect to their substitution pattern. Many of the enzymes used, such as Cel5A, Cel7B and Cel45 from Trichoderma reseei [15],[30], EGII from Trichoderma longibrachiatum [16], Cel5A from Bacillus agaradhaerens [24],[30],[38] or Cel5A from Humicola insolens [30] contain one or more carbohydrate-binding modules linked to either the C- or N-terminus of the catalytic module. The goal of this work was to investigate if CBMs on their own have the ability to make a distinction in the distribution pattern of cellulose derivatives based on their substitution pattern.

In this proof-of-concept study we show that CBMs indeed have the potential to be utilized in the characterization of chemically modified celluloses and can, due to the selective binding affinity displayed by the individual CBM, be used as tools to make a distinction between homogeneously and heterogeneously substituted MC and HPMC. The analysis was carried out using AE that provided a simple readout system. More extensive migration retardation of some CBMs, in particular CBM4-2, was observed in gels containing heterogeneously substituted cellulose derivatives. The molecular rationale for this behavior is not fully understood. The batches of cellulose derivatives with heterogeneous dispersed substituents might carry more binding epitopes and/or such of a nature that can create stronger binding affecting the overall CBM-cellulose polymer interaction, reflected in an increased retardation in the AE gels.

Visualization of CBM – carbohydrate interactions with affinity electrophoresis provides a rapid and easy read-out

Affinity gel electrophoresis is a technique that combines the visual simplicity of normal native gel electrophoresis with the specific separation of affinity interactions between various macromolecules. It has been widely used for the binding analysis of various interactions including those between antibody-hapten [39], lectin-glycoprotein [40] and between proteins and nucleic acids [41]. In 1977 AE was used to analyze the binding of a lectin against a soluble polysaccharide [42] and following the discovery of CBMs this protocol was adopted for studying the interaction of CBMs and polysaccharides [43]. Today AE is one of the most applied methods for rapid characterization of CBMs with unknown functions or for determining the role of a given amino acid after mutation [44]. In this study we show that this method not only provides information of the CBM but can also be used for the characterization of the polysaccharides. More specifically, the use of AE together with for example CBM4-2 has the potential to function as an initial screening method for the characterization of the substitution pattern of cellulose derivatives.

Future prospects

To establish a more detailed analysis of the substituent patterns of derivatized celluloses there are multiple possibilities to exploit in terms of a CBM/AE-based assay. An assay of this type may firstly rely on multiple readouts based not only on changes in CBMs’ retardation at a fixed carbohydrate gel content but also on their migration behavior at different concentrations of the derivatized carbohydrate. The second important window of opportunity is to be found in our ability to expand the set of CBMs to include an even more selective binding capacity and to create a multiplexed assay employing multiple CBMs. Such CBM candidates may potentially be of natural origin and found linked to cellulases, but new CBMs can also be obtained through engineering, specifically designed to suit this application. Direct evolution and rational design are powerful approaches for the fine-tuning of protein properties, and a combination of the use of combinatorial libraries and phage-display technology has been successful for the generation of engineered CBMs [34] toward other carbohydrate polymers including xylans [45] and different molecular forms of xyloglucan [46],[47]. In the present study CBMs engineered for such natural substrates were included but were unable or inefficient in their ability to discriminate between differentially substituted forms of cellulose. These results were not unexpected since the engineered CBM had not been specifically designed for this application but instead for recognition of other carbohydrate targets. In a future assay one could consider simultaneous use of CBMs that not only represent binders that discriminate substitutions, but also CBMs that specifically interact with these chemical groups, permitting a more complete mapping of the derivatized celluloses. We envisage that engineering of modules with predetermined tolerance for substitutions will be a valuable approach in the implementation of an assay for characterization of cellulose derivatives. It is expected, based on past experience on evolution of CBM binding properties [34],[45],[46],[48], that an appropriately designed phage-display selection process will be able to identify variants from combinatorial libraries that are able to differentiate between differently substituted celluloses. Such engineering will improve assay functionality over the current proof-of-concept study that employed non-optimized CBMs only.

Conclusion

In conclusion, this study demonstrates that some CBMs have the ability to discriminate between batches of cellulose derivatives with differences in substitution homogeneity. We anticipate that CBMs with better capacity to characterize carbohydrate polymers can be identified from natural sources or created in vitro and that such modules can be implemented in a non-degrading screening assay that can complement today’s standard analysis for use in quality control of batches of industrial cellulose derivatives.

Methods

Carbohydrate-binding modules

CBM4-2 from Rhodothermus marinus xylanase 10A and evolved CBM X-2 L110F [35] were produced in E. coli T7 Express (New England Biolabs, Ipswich, England) and purified using affinity chromatography columns on a Ni-NTA resin (Qiagen, Hilden, Germany) as previously described [35]. A codon-optimized gene (synthesized by GeneArt, Life Technologies, Carlsbad, CA, USA) coding for amino acids 571–762 of Bacillus akibai (also known as Bacillus sp. 1139) cellulase 5A, representing CBM28 [33], carried in the pET22b(+) vector (Novagen, Madison, WI, USA) was transformed into E. coli T7 Express. Protein production was made in 200 ml 2 x Yeast Tryptone broth supplemented with 100 μg/ml carbenicillin. The bacteria were cultivated at 37°C with shaking (210 rpm) until OD600 nm reached 0.4. Protein production was induced by addition of 0.5 mM isopropyl-β-D-thiogalactopyranoside followed by a further cultivation at 30°C with shaking (210 rpm) for 4 hours. A-6, which was evolved from CBM4-2 and selected, using phage-display, for its ability to recognize Avicel [34], and G-4, which was also evolved from CBM4-2 but has no carbohydrate-binding activity and is used as negative control [34],[36], were produced in E. coli BL21(λDE3) as previously described [34].

In an effort to create proteins with stronger binding to cellulose derivatives, we constructed and produced proteins consisting of two CBMs fused together via a peptide linker. Codon-optimized genes encoding such in tandem coupled CBMs carried in the pET22b(+) vector (Novagen) were purchased from GeneArt. The CBMs fused in tandem were produced in E. coli T7 Express as described above.

Cellulose derivatives

Three methylcelluloses were used in this study: MC 1.76 (viscosity type 4 cP), MC 1.78 (viscosity type 15 cP) and MC 1.80 (viscosity type 1500) from Shin-Etsu Chemical Co. (Tokyo, Japan) with similar degree of substitution (DS 1.76, 1.78 and 1.80, respectively) but with different molecular weights (20, 40 respectively 200 kDa) as analyzed by Melander et al. [49], Cohen et al. [24] and Fitzpatrick et al. [23]. The substitution patterns of the MCs have previously been characterized. MC 1.76 is more homogeneously substituted while MC 1.78 and MC 1.80 are more heterogeneously substituted [24]. Four hydroxypropyl methylcellulose (HPMC) batches were also analyzed. Of the HPMC used, batches 20 and 22 were from Dow Wolff Cellulosics (Bomlitz, Germany) and 21 and 23 from Shin-Etsu Chemical Co. All four batches had a similar degree of substitution and molecular weight but batches 21 and 23 were less susceptible to enzymatic degradation, performed with Celluclast (Novozymes A/S, Bagsvaerd, Denmark) and have therefore been classified as homogeneously substituted. Batches 20 and 22 on the other hand were more easily degraded thus classified as carrying a more heterogeneous substitution pattern.

Affinity electrophoresis

Affinity electrophoresis was used to determine the ability of soluble, charged, mobile CBMs to interact with largely immobile carbohydrates (and thus to become less mobile) under the influence of an electric field. Polyacrylamide gels for analysis of native proteins were cast according to the Ornstein-Davis method [50],[51] with the important modification of the addition of polysaccharides. The retardation of the CBM (3 μg/lane) was investigated using gels containing MC or HPMC at a concentration of 3 and 1 mg/ml, respectively. The gels were polymerized in cassettes (Life Technologies) at an acrylamide/bisacrylamide concentration of 12.5/0.42% for gels containing MC and 17.5/0.58% for gels containing HPMC and run in a minigel system for 1 hour and 45 minutes. Staining of protein was done with SimplyBlue (Life Technologies) for 20 minutes, followed by destaining in water according to the manufacturer’s instructions.

Abbreviations

CBM:

Carbohydrate-binding module

AE:

Affinity electrophoresis

HPMC:

Hydroxypropyl methyl cellulose

MC:

Methyl cellulose

HPC:

Hydroxypropyl cellulose

HEC:

Hydroxyethyl cellulose

CMC:

Carboxymethyl cellulose

MS:

Mass spectrometry

NMR:

Nuclear magnetic resonance

MALDI-ToF:

Matrix-assisted laser desorption/ionizaion time of flight)

ESI:

Electrospray ionization

References

  1. Kamel S, Ali N, Jahangir K, Shah SM, El-Gendy AA: Pharmaceutical significance of cellulose: a review. Express Polym Lett. 2008, 2: 758-778. 10.3144/expresspolymlett.2008.90.

    Article  CAS  Google Scholar 

  2. Medronho B, Romano A, Miguel MG, Stigsson L, Lindman B: Rationalizing cellulose (in)solubility: reviewing basic physicochemical aspects and role of hydrophobic interactions. Cellulose. 2012, 19: 581-587. 10.1007/s10570-011-9644-6.

    Article  CAS  Google Scholar 

  3. Chang CY, Zhang LN: Cellulose-based hydrogels: present status and application prospects. Carbohydr Polym. 2011, 84: 40-53. 10.1016/j.carbpol.2010.12.023.

    Article  CAS  Google Scholar 

  4. Maderuelo C, Zarzuelo A, Lanao JM: Critical factors in the release of drugs from sustained release hydrophilic matrices. J Control Release. 2011, 154: 2-19. 10.1016/j.jconrel.2011.04.002.

    Article  CAS  Google Scholar 

  5. Tran PH, Tran TT, Park JB, Lee BJ: Controlled release systems containing solid dispersions: strategies and mechanisms. Pharm Res. 2011, 28: 2353-2378. 10.1007/s11095-011-0449-y.

    Article  CAS  Google Scholar 

  6. Li CL, Martini LG, Ford JL, Roberts M: The use of hypromellose in oral drug delivery. J Pharm Pharmacol. 2005, 57: 533-546. 10.1211/0022357055957.

    Article  CAS  Google Scholar 

  7. Gao P, Skoug JW, Nixon PR, Ju TR, Stemm NL, Sung KC: Swelling of hydroxypropyl methylcellulose matrix tablets. 2. Mechanistic study of the influence of formulation variables on matrix performance and drug release. J Pharm Sci. 1996, 85: 732-740. 10.1021/js9504595.

    Article  CAS  Google Scholar 

  8. Kavanagh N, Corrigan OI: Swelling and erosion properties of hydroxypropylmethylcellulose (Hypromellos) matrices - influence of agitation rate and dissolution medium composition. Int J Pharm. 2004, 279: 141-152. 10.1016/j.ijpharm.2004.04.016.

    Article  CAS  Google Scholar 

  9. Reynolds TD, Gehrke SH, Hussain AS, Shenouda LS: Polymer erosion and drug release characterization of hydroxypropyl methylcellulose matrices. J Pharm Sci. 1998, 87: 1115-1123. 10.1021/js980004q.

    Article  CAS  Google Scholar 

  10. Novak SD, Kuhelj V, Vrecer F, Baumgartner S: The influence of HPMC viscosity as FRC parameter on the release of low soluble drug from hydrophylic matrix tablets. Pharm Dev Technol. 2013, 18: 343-347. 10.3109/10837450.2011.609991.

    Article  CAS  Google Scholar 

  11. Adden R, Muller R, Mischnick P: Analysis of the substituent distribution in the glucosyl units and along the polymer chain of hydroxypropylmethyl celluloses and statistical evaluation. Cellulose. 2006, 13: 459-476. 10.1007/s10570-005-9028-x.

    Article  CAS  Google Scholar 

  12. Enebro J, Momcilovic D, Siika-aho M, Karlsson S: Liquid chromatography combined with mass spectrometry for the investigation of endoglucanase selectivity on carboxymethyl cellulose. Carbohyd Res. 2009, 344: 2173-2181. 10.1016/j.carres.2009.08.009.

    Article  CAS  Google Scholar 

  13. Mischnick P, Momcilovic D: Chemical structure analysis of starch and cellulose derivatives. Adv Carbohyd Chem Biochem. 2010, 64: 117-210. 10.1016/S0065-2318(10)64004-8.

    Article  CAS  Google Scholar 

  14. Schagerlöf H, Richardson S, Momcilovic D, Brinkmalm G, Wittgren B, Tjerneld F: Characterization of chemical substitution of hydroxypropyl cellulose using enzymatic degradation. Biomacromolecules. 2006, 7: 80-85. 10.1021/bm050430n.

    Article  Google Scholar 

  15. Viridén A, Larsson A, Schagerlöf H, Wittgren B: Model drug release from matrix tablets composed of HPMC with different substituent heterogeneity. Int J Pharm. 2010, 401: 60-67. 10.1016/j.ijpharm.2010.09.017.

    Article  Google Scholar 

  16. Viridén A, Wittgren B, Andersson T, Larsson A: The effect of chemical heterogeneity of HPMC on polymer release from matrix tablets. Eur J Pharm Sci. 2009, 36: 392-400. 10.1016/j.ejps.2008.11.003.

    Article  Google Scholar 

  17. Viridén A, Larsson A, Wittgren B: The effect of substitution pattern of HPMC on polymer release from matrix tablets. Int J Pharm. 2010, 389: 147-156. 10.1016/j.ijpharm.2010.01.029.

    Article  Google Scholar 

  18. Heinze T, Koschella A: Carboxymethyl ethers of cellulose and starch - a review. Macromol Symp. 2005, 223: 13-39. 10.1002/masy.200550502.

    Article  CAS  Google Scholar 

  19. Mischnick P, Heinrich J, Gohdes M, Wilke O, Rogmann N: Structure analysis of 1,4-glucan derivatives. Macromol Chem Physic. 2000, 201: 1985-1995. 10.1002/1521-3935(20001001)201:15<1985::AID-MACP1985>3.0.CO;2-4.

    Article  CAS  Google Scholar 

  20. Tezuka Y, Tsuchiya Y: Determination of substituent distribution in cellulose acetate by means of a 13C NMR study on its propanoated Derivative. Carbohyd Res. 1995, 273: 83-91. 10.1016/0008-6215(95)00107-5.

    Article  CAS  Google Scholar 

  21. Arisz PW, Kauw HJJ, Boon JJ: Substituent distribution along the cellulose backbone in O-methylcelluloses using GC and FAB-MS for monomer and oligomer analysis. Carbohyd Res. 1995, 271: 1-14. 10.1016/0008-6215(95)00039-V.

    Article  CAS  Google Scholar 

  22. Saake B, Horner S, Kruse T, Puls J, Liebert T, Heinze T: Detailed investigation on the molecular structure of carboxymethyl cellulose with unusual substitution pattern by means of an enzyme-supported analysis. Macromol Chem Physic. 2000, 201: 1996-2002. 10.1002/1521-3935(20001001)201:15<1996::AID-MACP1996>3.0.CO;2-X.

    Article  CAS  Google Scholar 

  23. Fitzpatrick F, Schagerlöf H, Andersson T, Richardson S, Tjerneld F, Wahlund KG, Wittgren B: NMR, cloud-point measurements and enzymatic depolymerization: complementary tools to investigate substituent patterns in modified celluloses. Biomacromolecules. 2006, 7: 2909-2917. 10.1021/bm060281o.

    Article  CAS  Google Scholar 

  24. Cohen AS, Nilsson C, Schagerlöf H, Tjerneld F, Gorton L: Investigation of the enzyme Bacillus agaradhaerens Cel 5a as an analytical tool in mass spectral characterisation of methylcelluloses. Anal Chim Acta. 2006, 561: 16-24. 10.1016/j.aca.2006.01.019.

    Article  CAS  Google Scholar 

  25. Cuers J, Unterieser I, Burchard W, Adden R, Rinken M, Mischnick P: Simultaneous determination of substituent patterns in partially acid hydrolyzed O-Me/O-Me-d(3)-cellulose and quantification of the obtained oligomers by HPLC-ESI-MS. Carbohyd Res. 2012, 348: 55-63. 10.1016/j.carres.2011.11.016.

    Article  CAS  Google Scholar 

  26. Adden R, Melander C, Brinkmalm G, Gorton L, Mischnick P: New approaches to the analysis of enzymatically hydrolyzed methyl cellulose. Part 1. Investigation of the influence of structural parameters on the extent of degradation. Biomacromolecules. 2006, 7: 1399-1409. 10.1021/bm050941+.

    Article  CAS  Google Scholar 

  27. Unterieser I, Mischnick P: Labeling of oligosaccharides for quantitative mass spectrometry. Carbohyd Res. 2011, 346: 68-75. 10.1016/j.carres.2010.11.001.

    Article  CAS  Google Scholar 

  28. Greiderer A, Steeneken L, Aalbers T, Vivo-Truyols G, Schoenmakers P: Characterization of hydroxypropylmethylcellulose (HPMC) using comprehensive two-dimensional liquid chromatography. J Chromatogr A. 2011, 1218: 5787-5793. 10.1016/j.chroma.2011.04.076.

    Article  CAS  Google Scholar 

  29. Schagerlöf H, Johansson M, Richardson S, Brinkmalm G, Wittgren B, Tjerneld F: Substituent distribution and clouding behavior of hydroxypropyl methyl cellulose analyzed using enzymatic degradation. Biomacromolecules. 2006, 7: 3474-3481. 10.1021/bm0604799.

    Article  Google Scholar 

  30. Schagerlöf U, Schagerlöf H, Momcilovic D, Brinkmalm G, Tjerneld F: Endoglucanase sensitivity for substituents in methyl cellulose hydrolysis studied using MALDI-TOFMS for oligosaccharide analysis and structural analysis of enzyme active sites. Biomacromolecules. 2007, 8: 2358-2365. 10.1021/bm0701200.

    Article  Google Scholar 

  31. Boraston AB, Bolam DN, Gilbert HJ, Davies GJ: Carbohydrate-binding modules: fine-tuning polysaccharide recognition. Biochem J. 2004, 382: 769-781. 10.1042/BJ20040892.

    Article  CAS  Google Scholar 

  32. Simpson PJ, Jamieson SJ, Abou-Hachem M, Karlsson EN, Gilbert HJ, Holst O, Williamson MP: The solution structure of the CBM4-2 carbohydrate binding module from a thermostable Rhodothermus marinus xylanase. Biochemistry. 2002, 41: 5712-5719. 10.1021/bi012093i.

    Article  CAS  Google Scholar 

  33. Boraston AB, Ghaffari M, Warren RAJ, Kilburn DG: Identification and glucan-binding properties of a new carbohydrate-binding module family. Biochem J. 2002, 361: 35-40. 10.1042/0264-6021:3610035.

    Article  CAS  Google Scholar 

  34. Cicortas-Gunnarsson L, Nordberg-Karlsson E, Albrekt AS, Andersson M, Holst O, Ohlin M: A carbohydrate binding module as a diversity-carrying scaffold. Protein Eng Des Sel. 2004, 17: 213-221. 10.1093/protein/gzh026.

    Article  CAS  Google Scholar 

  35. von Schantz L, HĂĄkansson M, Logan DT, Walse B, Ă–sterlin J, Nordberg-Karlsson E, Ohlin M: Structural basis for carbohydrate-binding specificity-A comparative assessment of two engineered carbohydrate-binding modules. Glycobiology. 2012, 22: 948-961. 10.1093/glycob/cws063.

    Article  CAS  Google Scholar 

  36. Cicortas-Gunnarsson L, Dexlin L, Nordberg-Karlsson E, Holst O, Ohlin M: Evolution of a carbohydrate binding module into a protein-specific binder. Biomol Eng. 2006, 23: 111-117. 10.1016/j.bioeng.2005.12.002.

    Article  Google Scholar 

  37. Bolam DN, Xie H, White P, Simpson PJ, Hancock SM, Williamson MP, Gilbert HJ: Evidence for synergy between family 2b carbohydrate binding modules in Cellulomonas fimi xylanase 11A. Biochemistry. 2001, 40: 2468-2477. 10.1021/bi002564l.

    Article  CAS  Google Scholar 

  38. Momcilovic D, Schagerlöf H, Rome D, Jornten-Karlsson M, Karlsson KE, Wittgren B, Tjerneld F, Wahlund KG, Brinkmalm G: Derivatization using dimethylamine for tandem mass spectrometric structure analysis of enzymatically and acidically depolymerized methyl cellulose. Anal Chem. 2005, 77: 2948-2959. 10.1021/ac048194e.

    Article  CAS  Google Scholar 

  39. Tanaka T, Suzuno R, Nakamura K, Kuwahara A, Takeo K: Thermodynamic analysis of the interactions of a mouse dinitrophenyl-specific myeloma protein, MOPC-315, with immobilized dinitrophenyl and trinitrophenyl ligands by affinity electrophoresis. Electrophoresis. 1986, 7: 204-209. 10.1002/elps.1150070503.

    Article  CAS  Google Scholar 

  40. Nakamura S, Tanaka K, Murakawa S: Specific protein of legumes which reacts with animal proteins. Nature. 1960, 188: 144-145. 10.1038/188144b0.

    Article  CAS  Google Scholar 

  41. Takeo K: Affinity electrophoresis - principles and applications. Electrophoresis. 1984, 5: 187-195. 10.1002/elps.1150050402.

    Article  CAS  Google Scholar 

  42. Horejsi V, Ticha M, Kocourek J: Studies on lectins. XXXI. Determination of dissociation constants of lectin sugar complexes by means of affinity electrophoresis. Biochim Biophys Acta. 1977, 499: 290-300. 10.1016/0304-4165(77)90011-3.

    Article  CAS  Google Scholar 

  43. Tomme P, Boraston A, Kormos JM, Warren RAJ, Kilburn DG: Affinity electrophoresis for the identification and characterization of soluble sugar binding by carbohydrate-binding modules. Enzyme Microb Tech. 2000, 27: 453-458. 10.1016/S0141-0229(00)00246-5.

    Article  CAS  Google Scholar 

  44. Abbott DW, Boraston AB: Quantitative approaches to the analysis of carbohydrate-binding module function. Methods Enzymol. 2012, 510: 211-231. 10.1016/B978-0-12-415931-0.00011-2.

    Article  CAS  Google Scholar 

  45. Cicortas-Gunnarsson L, Montanier C, Tunnicliffe RB, Williamson MP, Gilbert HJ, Nordberg-Karlsson E, Ohlin M: Novel xylan-binding properties of an engineered family 4 carbohydrate-binding module. Biochem J. 2007, 406: 209-214. 10.1042/BJ20070128.

    Article  CAS  Google Scholar 

  46. Cicortas Gunnarsson L, Zhou Q, Montanier C, Nordberg Karlsson E, Brumer H, Ohlin M: Engineered xyloglucan specificity in a carbohydrate-binding module. Glycobiology. 2006, 16: 1171-1180. 10.1093/glycob/cwl038.

    Article  Google Scholar 

  47. von Schantz L, Håkansson M, Logan DT, Nordberg Karlsson E, Ohlin M: Carbohydrate binding module recognition of xyloglucan defined by polar contacts with branching xyloses and CH-π interactions. Proteins 2014, 82:3466–3475,

  48. von Schantz L, Gullfot F, Scheer S, Filonova L, Cicortas Gunnarsson L, Flint JE, Daniel G, Nordberg-Karlsson E, Brumer H, Ohlin M: Affinity maturation generates greatly improved xyloglucan-specific carbohydrate binding modules. BMC Biotechnol. 2009, 9: 92-10.1186/1472-6750-9-92.

    Article  Google Scholar 

  49. Melander C, Momcilovic D, Nilsson C, Bengtsson M, Schagerlöf H, Tjerneld F, Laurell T, Reimann CT, Gorton L: Microchip immobilized enzyme reactors for hydrolysis of methyl cellulose. Anal Chem. 2005, 77: 3284-3291. 10.1021/ac050201r.

    Article  CAS  Google Scholar 

  50. Ornstein L: Disc electrophoresis - I Background and theory. Ann NY Acad Sci. 1964, 121: 321-10.1111/j.1749-6632.1964.tb14207.x.

    Article  CAS  Google Scholar 

  51. Davis BJ: Disc electrophoresis - II Method and application to human serum proteins. Ann NY Acad Sci. 1964, 121: 404-427. 10.1111/j.1749-6632.1964.tb14213.x.

    Article  CAS  Google Scholar 

Download references

Acknowledgements

The study was supported by a grant from the Swedish Research Council (grant number: 621-2009-5152) and a grant from the European Commission (FP7, KBBE.2012.3.2-01, grant number 311932).

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Mats Ohlin.

Additional information

Competing interest

The authors declare that they have no competing interest.

Authors’ contributions

LvS, HS and MO conceived the study; LvS, HS and MO contributed critical, unique research reagents; LvS performed the experiments; LvS, ENK, HS and MO analyzed the results; LvS wrote the manuscript; LvS, ENK, HS and MO approved the final version of the manuscript. All authors read and approved the final manuscript.

Authors’ original submitted files for images

Rights and permissions

Open Access  This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.

The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.

To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.

The Creative Commons Public Domain Dedication waiver (https://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

von Schantz, L., Schagerlöf, H., Nordberg Karlsson, E. et al. Characterization of the substitution pattern of cellulose derivatives using carbohydrate-binding modules. BMC Biotechnol 14, 113 (2014). https://doi.org/10.1186/s12896-014-0113-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s12896-014-0113-9

Keywords